| 固化前特性 | 項(xiàng)目 | 數(shù)值 | 固化后特性 | 項(xiàng)目 | 數(shù)值 |
| 外觀 | Aside透明液體 | 硬度 | 58shoreD | ||
| Appearamce | Hardness | ||||
| Bside透明液體 | 折射率 | 1.54 | |||
| Refractindex | |||||
| 密度 | Aside1.01 | 透光率(450nm/1mm) | 98% | ||
| Densityg/cm3 | Lighttransmittance | ||||
| Bside1.04 | 拉伸強(qiáng)度MPa | 7.5 | |||
| Tensilestrength | |||||
| 粘度 | Aside640 | 延伸率% | 20 | ||
| Viscaosity(25℃,mp.s) | Coefficientof | ||||
| extension | |||||
| Bside20000 | 體積膨脹系數(shù) | 190ppm/℃ | |||
| Volumeexpansion | |||||
| coefficient | |||||
| Mixed9800 | 體積電阻率 | >1×1014Ω.cm | |||
| Volumeresistiviy | |||||
| 可操作時(shí)間 | 180 | 介電常數(shù) | 3(60Hz) | ||
| Useaveilabetime(25℃,minutes) | Dielectricconstant | ||||
| 使用條件 | 混合比例 | 1:10 | 擊穿電壓 | 20~25Kv/mm | |
| MixingratioA:B | Punchthroughvoltage | ||||
| 標(biāo)準(zhǔn)固化條件 | 90℃×1h,150℃× | 彈性模量MPa | 152 | ||
| Standardcuringconditions | 3h | Modulusofealasticity |
04-10
熱烈慶祝萬木新材料成立十五周年
2010.3-2025.3萬”象更新十五載 木”秀于林創(chuàng)未來 總經(jīng)理張文彬先生致詞 15年風(fēng)雨兼程，15年春華秋實(shí)，在這里我要深深的感謝我們?nèi)f木的兄弟姐妹們，感謝你們一直以來對(duì)我的信任與陪伴，感謝你們風(fēng)風(fēng)雨雨，不
07-19
賀：研發(fā)中心&EMC車間喬遷之喜
2024年7月10日13:58吉時(shí)，在萬木新材料工業(yè)園區(qū)，隆重舉行了研發(fā)中心&EMC生產(chǎn)車間新址啟用暨喬遷揭儀式。特邀嘉賓、公司管理層以及公司部分員工參加儀式，共同見證這一公司發(fā)展史上具有里程碑意義的重要時(shí)刻